1 Part Non-Corrosive Neutral Cure Adhesive Sealant and Coating (Electronic Grade)
Feature
  • Non corrosive
  • Excellent adhesion to most substrates
  • Excellent dielectric and isolating properties
  • Low odour
Code
AS1700
Feature
Feature 1
Non corrosive
Feature 2
Excellent adhesion to most substrates
Feature 3
Excellent dielectric and isolating properties
Feature 4
Low odour
100% Modulus (N/mm2)
0.61 MPa
Appearance
Thixotropic paste
Colour
Translucent
Cure Through to 3 mm Depth
36 hr
Cure Type
Alkoxy
Density
1.1 g/cm3
Dielectric Constant
3
Dielectric Strength (V/mil)
457 V/mil
Dielectric Strength kV/mm
18 kV/mm
Dissipation Factor
0.0025
Drying / Fixing Conditions
23+/-2°C and 50+/-5% humidity
Elongation at Break (%)
545 %
Extrusion Rate g/min
290 g/min
Hardness Shore A
30
Lap Shear Aluminium kg/cm²
4.00 kg/cm²
Lap Shear Copper kg/cm²
3.98 kg/cm²
Lap Shear Polycarbonate Steel kg/cm²
5.22 kg/cm²
Lap Shear Stainless Steel 304 kg/cm²
3.04 kg/cm²
Linear Coefficient of Thermal Expansion (ppm/°C)
270 ppm/°C
Linear Shrinkage (%)
1 %
Max Storage Temperature
40 °C
Max Working Temp (°C)
200 °C
Min Working Temp (°C)
-50 °C
Rheology
Paste
RTV or Heat cure
RTV
Self Bonding
Yes
Shelf Life (mths)
12
Slump
1 mm/5mins
Tack Free Time / Skin Formation at 23°C/73°F
10 min
Tear Resistance (N/mm)
12.3 N/mm
Tensile Strength (N/mm2)
2.43 N/mm2
Test Conditions
7 days at 23+/-2°C and 50+/-5% humidity
Thermal Conductivity (W/mK)
0.2 W/mK
Volume Coefficient of Thermal Expansion (ppm/°C)
810 ppm/°C
Volume Resistivity (Ohms cm)
2.20E+15 ohms cm
Youngs Modulus (N/mm2)
0.54 N/mm2